Weld Star Weldstar Dual Core HF600-G MIG Wire 1.2MM - 15KG

Weldstar Dual Core HF600-G MIG Wire 1.2MM - 15KG Features and Applications Seamless high fill copper coated tubular wire for semi-automatic applications. Ideal for hardfacing components subject to abrasion and moderate impact. Unique welder appeal. Deposition rate increased by up to 20% when compared to solid wire. Martensitic weld metal contains finely dispersed hard carbides ensuring an optimal balance between abrasion, friction and impact resistance. Abrasion resistance at service temperatures up to 450°C. Preheat will be determined by the application and whether micro cracking in the deposit is acceptable. According to the base material preheating in the range 150°C - 300°C may be necessary. Precision layer wound for superior wire feeding characteristics. Typically used on bucket teeth, bucket lips, bulldozer blades, crusher jaws, scraper blades, chutes, pump housings, conveyor screws, slide plates, gear teeth, crusher hammers, drilling bits, ploughshares, reamers etc. Test Certificates can be found online @wilkinsonstar247.com    Standards EN ISO 14700 - T Fe2   Chemical Composition % (Typical) C% Mn% Si% P% S% Cr%  Ni% 0.5 1.2 0.6 0.010 0.013 5.7 0.05               Mo% Cu% Fe% Co% V% W%   0.80 0.10 Bal 0.006 0.010 <0.09     Hardness (HRC) Current Type Hardness - First Layer Hardness - Third Layer DC+ 52-55 54-57 DC- 55-57 57-60 Peak hardness in the range 50-62 HRC could be achieved in three layers. Direct polarity negative reduces dilution and favours higher hardness. Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Wear Type Suitability   Welding Parameters Ømm Current (A) Voltage (V) 1.20 mm 110-300 16-32   Shielding Gases EN ISO 14175 - M12, M20, M21   Welding Positions EN ISO 6947 - PA, PB

Weld Star Weldstar Dual Core HF55-0 MIG Wire 15KG

Features and Applications Metal cored tubular wire for self-shielded metal arc hardfacing. High chromium cast iron deposit containing a high proportion of hard primary chromium carbides in a tough austenitic matrix. The deposit is suitable for hardfacing components subject to extremely severe abrasive wear and moderate impact. Relief checking is normal and does not affect the properties of the deposit. However it is recommended putting down only two layers unless impact loading is small. Multi-layer deposits are possible in specific applications. Precision layer wound for superior wire feeding characteristics. Typically used on gyratory crusher cones and mantles, catalyst pipes and valves, slurry pipes and valve bodies, dredge pump bodies, sand dredge parts, extruder screws, “barmac” crushers, mining and earthmoving equipment, blast furnace bells, brick muller tyres, crusher hammers and rolls, riddle plates, wear plates, drag line components, screw conveyors for cement, cone knives and shredders, etc Test Certificates can be found online @wilkinsonstar247.com    Standards EN ISO 14700 - T Fe15   Chemical Composition % (Typical) C% Mn% Si% P% S% 5.5 1.2 1.7 0.008 0.010           Cr% Ni% Mo% Fe% Nb% 28.0 0.15 0.04 Bal 0.020 Structure is primary carbides and eutectic carbides of the M7C3 type in an austenitic matrix.   Hardness (HRC) Current Type Hardness - Third Layer DC+ 58-64 Mechanical properties are approximate and may vary based on the heat, welding parameters and other factors.   Wear Type Suitability   Welding Parameters Ømm Current (A) Voltage (V) 1.20 mm 100-250 21-28 1.60 mm 160-320 24-30   Welding Positions EN ISO 6947 - PA

Weld Star HF600 Solid Hard Facing MIG Wire 15kg 300MM Metal Reel

Features and Applications Copper coated high alloy solid wire for hardfacing and overlay of all C-Mn steels. This alloy deposits a martensitic structured weld metal with a hardness of about 54-60 HRC. Excellent abrasion resistance to moderate impact and high toughness. The weld metal has a Cr-Si structure and if not tempered can only be machined by grinding. Mostly used with semiautomatic and automatic procedures. A buffer layer is essential with hard to weld steels. Precision layer wound for superior wire feeding characteristics. Typically used on excavators in the mining industry, cylinder crushers, pneumatic hammers, knives, cutting and cold working tools, crumbling jaws, anvils, caterpillars, screws, guide rollers, etc. Test Certificates can be found online @wilkinsonstar247.com    Typical Base Materials X45CrSi9-3, 4Xr9Si2, X45CrSi8, HNV1, HNV2, SUH11, X45CrSi 9-3, 401 S45, SUH 1, STR 1, 40Ch9S2** Illustrative, not exhaustive list   Standards EN ISO 14700 - S Fe 8 DIN 8555 - MSG 6-GZ-60-GP   Chemical Composition % (Typical) C% Mn% Si% S%       0.46 <0.60 3.05 <0.030                     Cu% P% Ni% Cr%       <0.25 <0.040 <0.50 9.10         Mechanical Properties Hardness (HRC) - 54 - 60 Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Shielding Gases EN ISO 14175 - M21   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF   Packaging Data Diameter Weight Spool Pallet Qty 1.00 mm 1.20 mm 15 Kg 15 Kg BS300 BS300 72 72 Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained, this information is subject to change without notice and can be only considered as suitable for general guidance.