Weld Star Weldstar Dual Core 316L-T1 MIG Wire 1.2MM - 15KG

Weldstar Dual Core 316L-T1 MIG Wire 1.2MM - 15KG Features and Applications Rutile flux cored stainless steel wire for gas-shielded arc welding. 19% chromium - 12% nickel - 3% molybdenum - low carbon deposit. Attractive bead appearance, automatic slag release, very good penetration and high productivity. Excellent X-ray soundness. Specifically designed for out-of-position welding. Maximum productivity for completion of vertical welds. Precision layer wound for superior wire feeding characteristics. Suitable for welding stainless steels with an alloy content between 16 to 21% Cr, 6 to 13% Ni and up to 3% Mo, stabilised and un-stabilised types. Test Certificates can be found online @wilkinsonstar247.com     Typical Base Materials AISI 316 316L 316LN 316Ti 318 UNS S31600 S31603 S31653 S31635 S31640 EN Symbol X5 CrNiMo 17-12-2 X2 CrNiMo 17-13-2 X2 CrNiMoN 17-12-2 X6 CrNiMoTi 17-12-2 X10CrNiMoNb 18-12 * Illustrative, not exhaustive list   Standards EN ISO 17633-A - T 19 12 3 L P M21 1 / T 19 12 3 L P C1 1 AWS A5.22 - E316LT1-4 - E316LT1-1   Chemical Composition % (Typical) C% Mn% Si% Cr% Ni% Mo % S% P% 0.03 1.40 0.80 19.0 12.0 2.90 0.008 0.020   Mechanical Properties (Typical) Shielding Gas M21   Tensile Strength 600 MPa   Yield Strength 490 MPa   Elongation 35%   Impact Strength 50 J   Test Temperature -60ºC   Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Welding Parameters Ømm Current (A) Voltage (V) 1.20 mm 130-270 22-35   Shielding Gases EN ISO 14175 - C1, M21   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF, PG

Weld Star Weldstar ER309LSi Stainless Steel MIG Wire 15KG

Features and Applications Austenitic stainless steel wire that has a low carbon content, which reduces the possibilities of intergranular carbide precipitation, while increasing the resistance to intergranular corrosion without the use of stabilisers such as niobium or titanium. Increased silicon content promotes weld pool fluidity to give a smooth deposit appearance. High temperature oxidation and corrosion resistance up to 300°C. Ideal for joining and overlay of stainless steels of similar composition, such as AISI 309 castings and for joining of 3Cr12. Good performance under carburising atmospheres. Precision layer wound for superior wire feeding characteristics. Typically used on buffer layers before hardfacing, dissimilar joints between ferritic and austenitic steels and or difficult to weld steels etc.    Typical Base Materials 42CrMo4, C45, 42MnV7, tool steels etc, 1.2780, 1.4541, 1.4550, 1.4710, 1.4712, 1.4713, 1.4724, 1.4729, 1.4740, 1.4741, 1.4742, 1.4746, 1.4762, 1.4745, 1.4825, 1.4826, 1.4828, 1.4832, 1.4878, X15CrNiSi20 12, G-X 40 CrNiSi209, AISI 446, AISI442, AISI309, UNS S30900, UNS S44200, UNS S4460* * Illustrative, not exhaustive list   Standards EN ISO 14343-A - G 23 12 L Si AWS A5.9 - ER 309LSi

Weld Star Weldstar ER308LSi Stainless Steel MIG Wire 15KG

Features and Applications Austenitic stainless steel wire that has a low carbon content, which reduces the possibilities of intergranular carbide precipitation. ER 308LSi is used to weld base metals of a similar chemical composition such as 304, 305 and 347 etc. Increased silicon content promotes weld pool fluidity to give a smooth deposit appearance. Ideal for applications requiring atmospheric corrosion resistance typically in urban and rural media’s. Good mechanical strength at sub-zero temperatures down to -196°C. Precision layer wound for superior wire feeding characteristics. Typically used on a wide range of applications including pipe work, plate fabrication and vessel production etc. Test Certificates can be found online @wilkinsonstar247.com    Typical Base Materials W.Nr:   1.4306, 1.4301, 1.4541, 1.4550, 1.4311, 1.4546, 1.4312, 1.4300, 1.4312, 1.4371, 1.4541, 1.4543, 1.4550, 1.4452* DIN: X2CrNi 19 11 (TP), X4CrNi 18 10 (TP), X6CrNiTi 18 10 (TP), X6CrNiNb 18 10 (TP), X2CrNiN 18 10 (TP), X5CrNiNb 18 10, G-X10CrNi 18 8 (TP)* AISI: 202, 302, 304L, 304, 305, 321, 347, 304 LN, ASTM A320 Grade B8C/D, 302* * Illustrative, not exhaustive list   Standards EN ISO 14343-A - G 19 9 LSi AWS A5.9 - ER 308LSi   Chemical Composition % (Typical) C% Mn% Si% S% P%     0.023 1.86 0.89 0.001 0.025                   Ni% Cr% Mo% Cu%       9.30 19.68 0.027 0.041         Mechanical Properties Tensile Strength ≥510 MPa   Yield Strength ≥320 MPa   Elongation ≥25 %   Impact Strength ≥80 J   Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Welding Parameters - M12 Ømm Current (A) Voltage (V) 0.80 mm 40-120 15-20 1.00 mm 80-160 16-22 1.20 mm 100-210 17-23   Welding Parameters - M13 Ømm Current (A) Voltage (V) 0.80 mm 160-210 24-28 1.00 mm 180-280 25-30 1.20 mm 200-300 26-32   Shielding Gases EN ISO 14175 - M12, M13   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF

Weld Star ER307Si Stainless Steel MIG Wire 15KG Reel

Features and Applications Austenitic stainless steel wire with a significant amount of manganese, making the all weld metal in most cases fully austenitic. High mechanical strength and excellent crack resistance. Increased silicon content promotes weld pool fluidity to give a smooth deposit appearance. Ideal for dissimilar welding between steel and stainless steel, armour plate and exhaust systems etc. Suitable for depositing stress relaxing buffer layers on crack sensitive base metals including hardfacing. Precision layer wound for superior wire feeding characteristics. Typically used on applications subject to atmospheric and corrosive media’s. Test Certificates can be found online @wilkinsonstar247.com    Typical Base Materials Armour plate, exhaust systems (type 409, 304), high Manganese austenitic steel, difficult to weld steels such as 42CrMo4, C45, 42MnV7, tool steels, 1.3401, X120Mn12 etc.* * Illustrative, not exhaustive list   Standards EN ISO 14343-A - G 18 8 Mn AWS A5.9 - ER 307Si   Chemical Composition % (Typical) C% Mn% Si% S% P%     0.045 6.06 0.82 0.005 0.029                   Ni% Cr% Mo% Cu%       8.02 18.35 0.05 0.030         Mechanical Properties Tensile Strength ≥500 MPa   Yield Strength ≥350 MPa   Elongation ≥25 %   Impact Strength ≥100 J   Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Welding Parameters - M12 Ømm Current (A) Voltage (V) 0.80 mm 40-120 15-20 1.00 mm 80-160 16-22 1.20 mm 100-210 17-23   Welding Parameters - M13 Ømm Current (A) Voltage (V) 0.80 mm 160-210 24-28 1.00 mm 180-280 25-30 1.20 mm 200-300 26-32   Shielding Gases EN ISO 14175 - M12, M13   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF   Liability: Whilst all reasonable efforts have been made to ensure the accuracy of the information contained, this information is subject to change without notice and can be only considered as suitable for general guidance.

BÖHLER Bohler 1.0MM Thermanit 2209 (ER2209) Duplex Stainless MIG Wire 15KG

Characteristics and typical fields of application Thermanit 2209 is primarily designed for welding the duplex grade 2205 and similar but it can also be used for SAF 2304 type of steels. Thermanit 2209 provides a ferritic-austenitic weldment that combines many of the good properties of both ferritic and austenitic stainless steels. The welding can be performed using short, spray or pulsed arc. Welding using pulsed arc provides good results in both horizontal and vertical-up positions. Structure: Austenite with 45 – 55 % ferrite. Scaling temperature: Approx. 850 °C (air). Corrosion resistance: Very good resistance to pitting and stress corrosion cracking in chloride containing environments.