Weld Star Weldstar 5356 AlMg5 Aluminium TIG Filler Rod 1.6, 2.4 & 3.2MM - 2.5KG Pack

Weldstar 5356 AlMg5 Aluminium TIG Filler Rod 1.6, 2.4 & 3.2MM - 2.5KG Pack Aluminium wire for welding aluminium alloys with a maximum 5% Magnesium. Features and Applications Excellent weldabillity and good mechanical strength, combined with good corrosion resistance in seawater conditions. AlMg5 is one of the most popular types of aluminium alloys. ER 5356 can also be used for welding components that need to be anodized. Thicker sections should be preheated to (150°C) prior to welding. Typically used on applications in the construction of boats, bicycles, trucks, pressure vessels, storage tanks, railways and automotive industries etc. Test Certificates can be found online @wilkinsonstar247.com    Typical Base Materials AlMg3, AlMg4, AlMg5,AlMgSi0.5, AlMgSi1; AlMgMn, AlZnMg1, G-AlMg3Si, G-AlMg5Si, G-AlMg10, AlMg1SiCu, AlMgSi0,7, AlZn4,5Mg1, AlSi1MgMn, AlSiMg(A), 3.3545, 3.3206, 3.3210, 3.2315, 3.3211, 3.4335, EN AW 5086, EN AW 6060, EN AW 6005A, EN AW , EN AW 6061, EN AW 7020, EN AC 51400, EN AC 51300, EN AC 51100, EN AW 5454* * Illustrative, not exhaustive list   Standards EN ISO 18273 - S Al 5356 (AlMg5Cr(A)) AWS A5.10 - ER 5356   Chemical Composition % (Typical) Si% Fe% Cu% Mn% Mg%     0.0401 0.1561 0.0014 0.1140 4.8277                   Cr% Zn% Ti% Be% Al%     0.1383 0.0048 0.0939 <0.0001 Rem.       Mechanical Properties Tensile Strength ≥235 MPa   Yield Strength ≥110 MPa   Elongation ≥17 %   Impact Strength ≥16 J   Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Shielding Gases EN ISO 14175 - TIG: I1, I3   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF, PG

Weld Star Weldstar ER4043 AlSi5 Aluminium TIG Filler Wire 1.6, 2.4 & 3.2MM - 2.5KG Pack

Weldstar 4043 AlSi5 Aluminium TIG Filler Wire 1.6, 2.4 & 3.2MM - 2.5KG Pack Aluminium TIG Filler wire for welding aluminium alloys with a maximum 2% alloying elements. Including aluminium alloys containing up to 7% Si. Features and Applications: The silicon addition results in improved fluidity (wetting action), making the alloy the preferred choice for welders. ER 4043 is not sensitive to weld cracking and produces bright, almost smut-free welds. Not recommended for anodizing. Thicker sections should be preheated to (150°C) prior to welding. Typically used on many industrial manufacturing sectors, such as automotive, production of mobile equipment and shipbuilding etc. Test Certificates can be found online @wilkinsonstar247.com    Typical Base Materials AlMgSi 0, AlSiMg (A), AlSi 1 MgMn, AlMg1SiCu, 3.3206, 3.3210, 3.2315, 3.3211, EN AW 6060, EN AW 6005A, EN AW 6082, EN AW 6061, EN AC 45000* * Illustrative, not exhaustive list   Standards EN ISO 18273 - S Al 4043 (AlSi5) AWS A5.10 - ER 4043   Chemical Composition % (Typical) Si% Fe% Cu% Mn% Mg%     5.0198 0.1578 0.0124 0.0035 0.0051                   Zn% Ti% Be% Al%       0.0036 0.0177 <0.0001 Rem.         Mechanical Properties Tensile Strength ≥120 MPa   Yield Strength ≥40 MPa   Elongation ≥8 %   Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Shielding Gases EN ISO 14175 - TIG: I1, I3   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF, PG