Weld Star Weldstar A32 ER0S-B2 Low Alloy TIG Filler Wire 5KG

Features and Applications Low alloy copper coated wire with 1.25% Cr and 1% Mo content used for the welding of heat-resistant steels. Suitable for welding 0.9% Cr and 0.5% Mo steels. Designed for high temperature power generation applications. Recommended working temperatures of up to 550°C. Typically used on equipment for the chemical and ammonia synthesis process, heat exchangers, boilers, pipes, pressure vessels, petrochemical industries etc. Green wire is produced using virgin raw materials sourced from specialised steel mills, which ensures consistent reliability and quality.    Typical Base Materials 13CrMo4-5, G17CrMo55, A387:2,11,12, A200: T11, T12, GS 25CrMo4, GS 18CrMo910, 10CrMo910, 10CrSiMoV7, 10CrV63, 12CrSiMo8** Illustrative, not exhaustive list   Standards EN ISO 21952-B - 1CM AWS A5.28 - ER 80S-B2   Chemical Composition % (Typical) C% Si% Mn% P% S% Cu% 0.08 0.55 0.60 <0.012 <0.015 <0.25             Cr% Ni% Mo% Al% V% Fx ppm 1.30 <0.20 0.50 <0.020 <0.010 <15

Weld Star Weldstar ER80S-Ni1 Low Temp Mild Steel TIG Filler Wire 5KG

Features and Applications Copper coated, Ni-alloy (1,0% Ni), solid wire for low temperature, fine grained and austempering steels. Excellent impact toughness due to the addition of Nickel. Good mechanical properties at sub-zero temperatures down to -50°C. Especially suitable for use in the offshore industry. Typically used on the building up of cranes, transport, tanks, industrial facilities, equipment in general, pipelines, shipbuilding etc. Green wire is produced using virgin raw materials sourced from specialised steel mills, which ensures consistent reliability and quality. Test Certificates can be found online @wilkinsonstar247.com    Typical Base Materials A106, A515, A714, A131, A369, A210, L290, P235 T1/T2, P275 T1 ; L360, L415; P275T2, P355N ; X-42, X46, X62, X60 ; P235GH, P355GH ; A283, A285, A414, A372, A662, S275, S420, A516, A255, A333, A350, A612** Illustrative, not exhaustive list   Standards EN ISO 14341-A - G 3Ni1 AWS A5.28 - ER 80S-Ni1   Chemical Composition % (Typical) C% Si% Mn% P% S% Cu% 0.09 0.70 1.20 <0.150 <0.150 <0.25             Cr% Ni% Mo% Al% V% Zr+Ti% <0.15 1.00 <0.15 <0.200 <0.030 <0.50   Mechanical Properties (Typical) Tensile Strength 600 MPa   Yield Strength 480 MPa   Elongation 26%   Impact Strength 100 J   Test Temperature -50ºC   Mechanical properties are approximate and may vary based on the heat, shielding gas, welding parameters and other factors.   Shielding Gases EN ISO 14175 - TIG: I1 (Argon)   Welding Positions EN ISO 6947 - PA, PB, PC, PD, PE, PF

BÖHLER Bohler Union 5356 ALMG5 Aluminium Tig Filler Rod 2.5KG

Böhler Union ALMG5(5356) Aluminium Magnesium TIG Filler Rods 5KG TIG welding rod for AlMg alloys containing up to 5 % Mg. High Strength: 5356 wire has relatively high tensile strength, making it suitable for applications where strength is a primary concern, such as in boat and shipbuilding, aerospace, and structural welding. Good Corrosion Resistance: This alloy offers good resistance to corrosion, which is vital for applications exposed to harsh environments, like marine or outdoor structures. Weldability: 5356 wire is known for its ease of use and smooth arc characteristics, making it suitable for both beginner and experienced welders. Low Melting Point: It has a lower melting point compared to some other aluminum alloys, which can help reduce the risk of burn-through or warping when welding thin aluminum materials. Anodizing Compatibility: 5356 aluminum is compatible with anodizing, which is a surface treatment process often used in various applications. Versatility: It can be used to weld various aluminum alloys, including 5052, 5083, 5086, 5154, and 6061. Spec: AWS A5.10 ER5356 Rod Diameter: 1.6mm, 2.4mm, 3.2mm Approvals: TÜV (2198.), DB (61.132.01)